This paper reports on measurements of the resistive transition in polycrystalline Gd1-χ Ceχ Ba2 Cu3 O7-δ samples (x = 0.000, 0.025 and 0.050). The samples were produced by a standard solid state reaction method and in two different thermal routes. The microstructure was analyzed by X-ray diffraction. The samples were considered homogeneous since no extra peaks due to impurity phase were observed. To identify power-law divergences in conductivity, the results were analyzed in terms of the temperature derivative of the resistivity and the logarithmic temperature derivative of the conductivity (d ln (Δσ) /dT). From the results, the occurrence of a two-stage transition besides the pairing transition splitting for sample with x = 0.050 was observed. Such splitting was associated with Ce doping and related with the occurrence of a phase separation. In the normal phase, Gaussian and critical fluctuations conductivity regimes were identified. Ón approaching the zero resistance state, our results showed a power-law behavior that corresponds to a phase transition from a paracoherent to a coherent state of the granular array.

In this work we report on conductivity fluctuation measurements in polycrystalline samples of the Er1-xPr xBa2Cu3O7-δ superconductor (x = 0.00, 0.05 and 0.10). Samples were prepared by a standard solid-state reaction technique. The results were analyzed in terms of the temperature derivative of the resistivity and of the logarithmic temperature derivative of the conductivity that allowed the identification of power-law divergences of the conductivity. The results show that the transition proceeds in two stages: pairing and coherence transition. Also, our results, from the critical exponent analysis, show a two-peak splitting at pairing transition, indicating possibly a phase separation. On approaching the zero resistance state, our results show a power-law behavior that corresponds to a phase transition from paracoherent to a coherent state of the granular array.